As Grown - No indication of post-growth treatment.This Laboratory Grown Diamond was created by High Pressure High Temperature (HPHT) growth process. Report Number 485127864 Report Type Lab Grown 4 Fold Description Laboratory Grown Diamond Weight IGI 6.47 Shape Square Cushion Modified Brilliant Table 62.00 Measurement 10.28 x 10.18 x 7.03 Polish Excellent SYM Very Good Clarity VS1 Color D Diamond Report Summary Report Number LG485127864 Report Date August 11, 2021   Description LABORATORY GROWN DIAMOND Shape And Cut SQUARE CUSHION MODIFIED BRILLIANT Grading Results Carat Weight 6.47 Carats Color Grade D Clarity Grade VS 1 Additional Grading Information Polish EXCELLENT Symmetry VERY GOOD Measurements 10.28 x 10.18 x 7.03 mm Table Size 62% Crown Height 15.5% - 39.1° Pavilion Depth 51% - 35° Girdle Thickness VERY THIN TO THICK (FACETED) Culet POINTED Total Depth 69.1% Fluorescence NONE Comments As Grown - No indication of post-growth treatmentThis Laboratory Grown Diamond was created by High Pressure High Temperature (HPHT) growth processType II Inscription(s) LABGROWN IGI LG485127864

As Grown - No indication of post-growth treatment.This Laboratory Grown Diamond was created by High Pressure High Temperature (HPHT) growth process. Report Number 485127864 Report Type Lab Grown 4 Fold Description Laboratory Grown Diamond Weight IGI 6.47 Shape Square Cushion Modified Brilliant Table 62.00 Measurement 10.28 x 10.18 x 7.03 Polish Excellent SYM Very Good Clarity VS1 Color D

Diamond Report Summary

Report Number LG485127864
Report Date August 11, 2021
 
Description LABORATORY GROWN DIAMOND
Shape And Cut SQUARE CUSHION MODIFIED BRILLIANT

Grading Results
Carat Weight 6.47 Carats
Color Grade D
Clarity Grade VS 1

Additional Grading Information
Polish EXCELLENT
Symmetry VERY GOOD
Measurements 10.28 x 10.18 x 7.03 mm
Table Size 62%
Crown Height 15.5% - 39.1°
Pavilion Depth 51% - 35°
Girdle Thickness VERY THIN TO THICK (FACETED)
Culet POINTED
Total Depth 69.1%
Fluorescence NONE
Comments As Grown - No indication of post-growth treatment
This Laboratory Grown Diamond was created by High Pressure High Temperature (HPHT) growth process
Type II
Inscription(s) LABGROWN IGI LG485127864